Q390合金管的性能及应用
| Q390是一种低合金高强度结构钢。
| 等级 |
C |
Mn |
Si |
P |
S |
V |
Nb |
Ti |
Al |
Cr |
Ni |
| A |
≦0.20 |
1.00～1.60 |
≦0.55 |
≦0.045 |
≦0.045 |
0.02～0.20 |
0.015～0.060 |
0.02～0.20 |
- |
≦0.30 |
≦0.70 |
| B |
≦0.20 |
1.00～1.60 |
≦0.55 |
≦0.040 |
≦0.040 |
0.02～0.20 |
0.015～0.060 |
0.02～0.20 |
- |
≦0.30 |
≦0.70 |
| C |
≦0.20 |
1.00～1.60 |
≦0.55 |
≦0.035 |
≦0.035 |
0.02～0.20 |
0.015～0.060 |
0.02～0.20 |
≧0.015 |
≦0.30 |
≦0.70 |
| D |
≦0.20 |
1.00～1.60 |
≦0.55 |
≦0.030 |
≦0.030 |
0.02～0.20 |
0.015～0.060 |
0.02～0.20 |
≧0.015 |
≦0.30 |
≦0.70 |
| E |
≦0.20 |
1.00～1.60 |
≦0.55 |
≦0.025 |
≦0.025 |
0.02～0.20 |
0.015～0.060 |
0.02～0.20 |
≧0.015 |
≦0.30 |
≦0.70 |
【抗拉强度】（σb/MPa）
490～650
【伸长率】（δ5/%）
| 等级 |
δ5/% |
| A |
≧19 |
| B |
≧19 |
| C |
≧20 |
| D |
≧20 |
| E |
≧20 |
【屈服点】（σs/MPa）
| 厚度（直径、边长）/mm |
≦16 |
>16～35 |
>35～50 |
>50～100 |
| σs/MPa |
≧390 |
≧370 |
≧350 |
≧330 |
【冲击吸收功】（Akv（纵向）/J）
| 等级￤温度 |
+20℃ |
0℃ |
-20℃ |
-40℃ |
| A |
|
|
|
|
| B |
≧34 |
|
|
|
| C |
|
≧34 |
|
|
| D |
|
|
≧34 |
|
| E |
|
|
|
≧27 |
【主要特性】
综合力学性能好，焊接性、冷、热加工性能和耐蚀性能均好，C、D、E级钢具有良好的低温韧性。
【应用举例】
船舶、锅炉、压力容器、石油储罐、桥梁、电站设备、起重运输机械及其他较高载荷的焊接结构件。 |
|
|
|
|